Use of polyetheresters for rotomolding

ABSTRACT

A densification aid for use in rotomolding or slush molding can include a major component and a minor component. The major component can include a polyetherester. The minor component can include a fluoropolymer, a thermoplastic polyurethane, a polyether block copolyamide or a polyethylene glycol. Articles can be formed using the densification aid, such as by rotomolding or slush molding a particulate olefin polymer composition with the densification aid.

FIELD OF THE INVENTION

The present invention relates to the use in rotomolding or in slush molding applications of a polyolefin composition comprising a processing aid and optionally a UV-stabilizer. The polyolefin composition can also be used for the production of articles by other processes such as injection molding, cast film, blown film, calendering, sheet extrusion.

BACKGROUND OF THE INVENTION

The present invention primarily concerns the fabrication of articles by rotomolding, also called rotational molding. In rotomolding a premeasured amount of polymer is placed in one half of the mold, the mold is closed and then heated until the polymer is molten. The mold is rotated so as to get good distribution of the polymer in the mold. The mold can be rotated either uniaxially or biaxially, but biaxial rotation is widely preferred, i.e. simultaneous rotation around two perpendicular axes. In the following the mold is cooled, opened and the formed article is removed from the mold. Rotomolding can also be used for multilayer molding, for example by using more than one polymer sequentially. Rotomolding allows the production of hollow articles with good wall thickness distribution and good mechanical properties.

Slush molding is a process that is closely related to rotomolding. In the following the term rotomolding is therefore used to imply both, rotomolding and slush molding applications.

The most widely used polymer in rotomolding is polyethylene. Therefore a lot of effort has been invested to improve the processability of polyethylene in rotomolding.

U.S. Pat. No. 6,362,270 discloses polymer compositions particularly suited for rotomolding. These polymer compositions comprise of at least 94% by weight of one or more thermoplastic polymers and a maximum of 6% by weight of one or more processing additives. The thermoplastic polymer may be selected from copolymers of ethylene and styrene, ethylene and/or C₃-C₂₀ alpha-olefin homo- or copolymers, nylon, polyethylene terephthalate, polycarbonate, acrylic polymer, polystyrene, and blends of these polymers. Suitable processing additives include aromatic or aliphatic hydrocarbon oils, esters, amides, alcohols, acids, and their organic or inorganic salts as well as silicone oils, polyether polyols, glycerol monostearate (GMS), pentaerytritol monooleate, erucamide, stearamides, adipic acid, sebacic acid, styrene-alpha-methyl-styrene, calcium stearate, zinc stearate, phthalates and blends thereof. The processing additive preferably decreases the composition's melt viscosity and/or elasticity at zero or low shear rates to allow for a reduction in sintering time, cycle time and/or maximum mold temperature.

A recent report (L. T. Pick, E. Harkin-Jones, Third Polymer Processing Symposium, 28-29, Jan. 2004, Belfast, p. 259-268) shows a correlation between the number of bubbles in a rotomolded article and its impact performance, with a higher number of bubbles resulting in lower impact performance. In addition, a high number of bubbles has a negative influence on the optical properties of the finished articles.

There is thus a need to provide a rotomolded article with a reduced number of bubbles.

There is also a need to provide a rotomolded article with improved optical properties.

There is also a need to provide a rotomolded article with improved mechanical properties.

It is an object of the present invention to provide a rotomolded article based on a polyolefin composition with improved processability in rotomolding applications.

It is another object of the present invention to provide a rotomolded article based on a polyolefin composition that improves the sintering and densification processes in rotomolding applications.

It is another object of the present invention to provide a rotomolded article based on a polyolefin composition that reduces bubble formation in the rotomolding process.

It is another object of the present invention to provide a rotomolded article based on a polyolefin composition that improves optical properties of the articles produced by rotomolding applications.

It is another object of the present invention to provide a rotomolded article based on a polyolefin composition that improves mechanical properties of the articles produced by rotomolding applications.

It is another object of the present invention to provide a rotomolded article based on a polyolefin composition that allows reducing cycle time in a rotomolding process.

It is another object of the present invention to provide a process for producing by rotomolding an article with improved properties.

It is yet another object of the present invention to provide a rotomolding process with improved densification and/or sintering processes.

SUMMARY OF THE INVENTION

Accordingly, the present invention provides rotomolded or slush molded articles prepared from a polyolefin composition essentially consisting of

-   -   (a) from 99% by weight to 99.999% by weight of         -   (i) a polyolefin or         -   (ii) a polyolefin composition comprising from 50% by weight             to 99% by weight of a first polyolefin and from 1% by weight             to 50% by weight of a different polymer,     -   (b) from 0.001% by weight to 1% by weight of a densification         aid;     -   (c) optionally from 0.025% by weight to 0.500% by weight of one         or more UV-stabilizers.

The present invention also discloses the use of that same composition in rotomolding and slush molding.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the temperature of air inside a mold expressed in degrees centigrade as a function of time expressed in minutes for a complete cycle in rotomolding applications.

FIG. 2 shows a camera set-up used to study sintering and densification behavior.

FIG. 3 represents a sequence of photographs showing the coalescence process.

FIG. 4 represents a series of photographs showing the bubble removal process.

DETAILED DESCRIPTION OF THE INVENTION

The densification aid comprises a polyetherester, optionally consisting essentially of a mixture of a polyetherester as major component with a minor component selected from the group consisting of polyether-black co-polyamide, thermoplastic polyurethane, polyethylene glycol and fluoropolymer.

By major component it is meant that such a component makes up more than 50% by weight. By minor component it is meant that such a component makes up less than 50% by weight.

Polyether-block co-polyamides are represented by the general formula HO—[C(O)—PA-C(O)—O-PEth-O]_(n)—H  (I) wherein PA represents the polyamide segment and PEth the polyether segment. For example the polyamide segment can be a PA 6, PA 66, PA 11 or a PA 12. The polyether segment can for example be a polyethylene glycol (PEG) or a polypropylene glycol (PPG) or a polytetramethylenglycol (PTMG). The molecular weight M_(n) of the polyamide sequence is usually between 300 and 15,000. The molecular weight M_(n) of the polyether sequence is usually between 100 and 6000. Such materials are commercially available for example from Atofina under the Pebax® trade name.

The copolymers having polyamide blocks and polyether blocks are generally obtained from the polycondensation of polyamide blocks having reactive end groups with polyether blocks having reactive end groups, such as, inter alia:

-   -   1) polyamide blocks having diamine chain ends with         polyoxyalkylene blocks having dicarboxylic chain ends;     -   2) polyamide blocks having dicarboxylic chain ends with         polyoxyalkylene blocks having diamine chain ends, obtained by         cyanoethylation and hydrogenation of aliphatic dihydroxylated         α,ω-polyoxyalkylene blocks called polyetherdiols; and     -   3) polyamide blocks having dicarboxylic chain ends with         polyetherdiols, the products obtained being, in this particular         case, polyetheresteramides.

The polyamide blocks having dicarboxylic chain ends derive, for example, from the condensation of polyamide precursors in the presence of a chain-stopping carboxylic diacid.

The polyamide blocks having diamine chain ends derive, for example, from the condensation of polyamide precursors in the presence of a chain-stopping diamine.

The polymers having polyamide blocks and polyether blocks may also include randomly distributed units. These polymers may be prepared by the simultaneous reaction of the polyether and of the precursors of the polyamide blocks.

For example, a polyetherdiol, polyamide precursors and a chain-stopping diacid may be made to react together. A polymer is obtained which essentially has polyether blocks and polyamide blocks of very variable length, but in addition the various reactants that have reacted randomly, which are distributed in a random fashion along the polymer chain.

A polyether diamine, polyamide precursors and a chain-stopping diacid may also be made to react together. A polymer is obtained which has essentially polyether blocks and polyamide blocks of very variable length, but also the various reactants that have reacted randomly, which are distributed in a random fashion along the polymer chain.

The amount of polyether blocks in these copolymers having polyamide blocks and polyether blocks is advantageously from 10 to 70% and preferably from 35 to 60% by weight of the copolymer.

The polyetherdiol blocks may either be used as such and copolycondensed with polyamide blocks having carboxylic end groups, or they may be aminated in order to be converted into polyetherdiamines and condensed with polyamide blocks having carboxylic end groups. They may also be blended with polyamide precursors and a diacid chain stopper in order to make the polymers having polyamide blocks and polyether blocks with randomly distributed units.

The number-average molar mass M_(n) of the polyamide blocks is usually between 300 and 15,000, except in the case of the polyamide blocks of the second type. The mass M_(n) of the polyether blocks is usually between 100 and 6000.

As regards the polyetheresters, these are copolymers having polyester blocks and polyether blocks. They generally consist of soft polyether blocks, which are the residues of polyetherdiols, and of hard segments (polyester blocks), which usually result from the reaction of at least one dicarboxylic acid with at least one chain-extending short diol unit. The polyester blocks and the polyether blocks are generally linked by ester linkages resulting from the reaction of the acid functional groups of the acid with the OH functional groups of the polyetherdiol. The short chain-extending diol may be chosen from the group consisting of neopentyl glycol, cyclohexanedimethanol and aliphatic glycols of formula HO(CH₂)_(n)OH in which n is an integer varying from 2 to 10. Advantageously, the diacids are aromatic dicarboxylic acids having from 8 to 14 carbon atoms. Up to 50 mol % of the dicarboxylic aromatic acid may be replaced with at least one other dicarboxylic aromatic acid having from 8 to 14 carbon atoms, and/or up to 20 mol % may be replaced with a dicarboxylic aliphatic acid having from 2 to 12 carbon atoms.

As examples of dicarboxylic aromatic acids, mention may be made of terephthalic, isophthalic, dibenzoic, naphthalenedicarboxylic acids, 4,4′-diphenylenedicarboxylic acid, bis(p-carboxyphenyl)methane acid, ethylenebis(p-benzoic acid), 1,4-tetramethylenebis(p-oxybenzoic acid), ethylenebis(paraoxybenzoic acid) and 1,3-trimethylene bis(p-oxybenzoic acid). As examples of glycols, mention may be made of ethylene glycol, 1,3-trimethylene glycol, 1,4-tetramethylene glycol, 1,6-hexamethylene glycol, 1,3-propylene glycol, 1,8-octamethylene glycol, 1,10-decamethylene glycol and 1,4-cyclohexylenedimethanol. The copolymers having polyester blocks and polyether blocks are, for example, copolymers having polyether blocks derived from polyether dials, such as polyethylene glycol (PEG), polypropylene glycol (PPG) or polytetramethylene glycol (PTMG), dicarboxylic acid units, such as terephthalic acid, and glycol (ethanediol) or 1,4-butanediol units. The chain-linking of the polyethers and diacids forms soft segments while the chain-linking of the glycol or the butanediol with the diacids forms the hard segments of the copolyetherester. Such copolyetheresters are disclosed in patents EP 402 883 and EP 405 227. These polyetheresters are thermoplastic elastomers. They may contain plasticizers.

Polyetheresters can for example be obtained from Du Pont Company under the Hytrel® trademark.

As regards the polyurethanes, these in general consist of soft polyether blocks, which usually are residues of polyetherdiols, and hard blocks (polyurethanes), which may result from the reaction of at least one diisocyanate with at least one short diol. The short chain-extending diol may be chosen from the glycols mentioned above in the description of the polyether esters. The polyurethane blocks and polyether blocks are linked by linkages resulting from the reaction of the isocyanate functional groups with the OH functional groups of the polyether diol.

Thermoplastic polyurethanes can for example be obtained from Elastogran GmbH under the Elastollan® trade name or from Dow Chemical Company under the Pellethanee® trade name.

Polyethylene glycols have the general formula H—(OCH₂—CH₂—)_(n)OH  (I)

Polyethylene glycols are commercially available in a wide range of molecular weights and viscosities. Depending upon their molecular weights polyethylene glycols can be liquid or solid. The polyethylene glycols used in the present invention usually have an average molecular weight from 100 to 2000 g/mol and more preferably from 150 to 700 g/mol. Suitable polyethylene glycols can for example be obtained from Dow Chemical Company or BASF under the Carbowax® and Pluriol E® trade names.

The fluoropolymers suited as processing aid in the present invention are for example polymers of vinylidene fluoride (H₂C═CF₂) and/or copolymers of vinylidene fluoride and hexafluoropropylene (F₂C═CF—CF₃). Though the copolymers of vinylidene fluoride and hexafluoropropylene do not have elastomeric properties they are commonly referred to as “fluoroelastomers”. The content of the comonomer hexafluoropropylene in a fluoroelastomer is usually in the range of 30 to 40% by weight. Fluoropolymers suited as processing aids in the current invention are for example commercially available under the Dynamar®, Viton® and Kynar® trade names from Dyneon, DuPont-Dow Elastomers or Atofina.

Polyethylenes prepared with a Ziegler-Natta or with metallocene catalyst or with late transition metal catalyst systems are typically used in rotomolding applications. Other materials can also be used, such as for example polypropylene. Linear low density polyethylene is preferably used as disclosed for example in “Some new results on rotational molding of metallocene polyethylenes” by D. Annechini, E. Takacs and J. Vlachopoulos in ANTEC, vol. 1, 2001.

The preferred polyolefin used in the composition according to the present invention is a homo- or co-polymer of ethylene produced with a catalyst comprising a metallocene on a silica/aluminoxane support. More preferably, the metallocene component is ethylene-bis-tetrahydroindenyl zirconium dichloride or bis-(n-butyl-cyclopentadienyl) zirconium dichloride or dichloro-(dimethylsilylene)bis(2-methyl-4-phenyl-indenylidene) zirconium dichloride. The most preferred metallocene component is ethylene-bis-tetrahydroindenyl zirconium dichloride.

In this description, the term copolymer refers to the polymerization product of one monomer and one or more comonomers. Preferably the monomer and the one or more comonomers are alpha-olefins with two to ten carbon atoms, with monomer and comonomer(s) being different alpha-olefins. More preferably the monomer is either ethylene or propylene and the one or more comonomers are alpha-olefins with two to eight carbon atoms. Most preferably the monomer is ethylene and the comonomer is either 1-butene or 1-hexene.

The melt index of the polyethylene or polypropylene resin preferably used in the present invention typically falls in the following ranges:

-   -   If the polyolefin of the present invention is a homo- or         co-polymer of ethylene, its melt index MI2 is typically in the         range 0.1 to 25 dg/min, preferably in the range 0.5 to 15 dg/min         and most preferably in the range 1.5 to 10 dg/min. The MI2 is         measured according to ASTM D 1283 at a temperature of 190° C.         and a load of 2.16 kg.     -   If the polyolefin of the present invention is a homo- or         copolymer of propylene, its melt flow index (MFI) is typically         in the range 0.1 to 40 dg/min, preferably in the range 0.5 to 30         dg/min and most preferably in the range 1 to 25 dg/min. The MFI         is measured according to ASTM ID 1283 at a temperature of         230° C. and a load of 2.16 kg.

For the homo- and co-polymers of ethylene that can be used in the present invention, the density is typically in the range 0.910 to 0.975 g/ml and preferably in the range 0.915 to 0.955 g/ml, and most preferably in the range 0.925 to 0.945/ml. The density is measured according to ASTM D 1505 at 23° C.

The polyolefins of the present invention may also have a bi- or multimodal Molecular weight distribution, i.e. they may be a blend of two or more polyolefins with different molecular weight distributions, which can be blended either physically or chemically, i.e. produced sequentially in two or more reactors.

The polydispersity D of the polyolefins used in the present invention is defined as the ratio Mw/Mn of the weight average molecular weight Mw over the number average molecular weight Mn. It is in the range 2 to 20, preferably 2 to 8, more preferably less than or equal to 5, and most preferably less than or equal to 4, the latter range being typically associated with the preferred metallocene-prepared polyethylene resins.

The polyolefins of the present invention may also comprise other additives such as for example antioxidants, acid scavengers, antistatic additives, fillers, slip additives or anti-blocking additives.

When a polyolefin composition is used as starting material, the composition comprises:

-   -   from 50 to 99% by weight of a first polyolefin, preferably         polyethylene;     -   from 1 to 50% by weight of a second polymer, which is different         from the processing aid, and which is preferably selected from         the group consisting of polyamide, copolyamide, a second         polyolefin different from the first one, copolymers of ethylene         and vinyl acetate (EVA), copolymers of ethylene and vinyl         alcohol (EVOH), polystyrene, polycarbonate and polyvinyl         chloride (PVC).

It is also possible to use a polyolefin comprising a densification aid as one or more layers of a multilayered rotomolded article with the other layers comprising a polymer preferably selected from the group consisting of polyamide, copolyamide, a second polyolefin different from the first one, copolymers of ethylene and vinyl acetate (EVA), copolymers of ethylene and vinyl alcohol (EVOH), polystyrene, polycarbonate and polyvinyl chloride (PVC).

The one or more UV-stabilizers can be selected from any known UV-stabilizer known in the art. The preferred UV-stabilizers are hindered amine light stabilizers (HALS). Commercially available examples of HALS include Chimassorb® 944, Tinuvin® 622 or Tinuvin® 783 from Ciba Specialty Chemicals.

Surprisingly, it has been found that the addition of 0.001% by weight to 1% by weight of a processing aid Improves the processability of a polyolefin in rotomolding by modifying the sintering and the densification behavior.

The use of a processing aid according to the present invention results in cycle time reductions of at least 10%, preferably by at least 20%. In order to obtain the same number of bubbles in the rotomolded articles the peak internal air temperature (PIAT) can be reduced by at least 10 degrees centigrade.

Even more surprisingly, it has been found that the further addition of from 0.025% by weight to 0.500% by weight of one or more UV-stabilizers to the composition described hereabove comprising 0.001% by weight to 1% by weight of a processing aid even further improves the processability of the polyolefin in rotomolding.

It is believed that there is a synergy between the processing aid and the UV-stabilizer, and it is thus preferred to use both.

In rotomolding a premeasured amount of polymer is placed in one half of the mold, the mold is closed and then heated until the polymer is molten. The mold is rotated so as to get an even distribution of the polymer in the mold. The mold can be rotated either uniaxially or biaxially, but biaxial rotation is widely preferred, i.e. simultaneous rotation around two perpendicular axes. In the following step the mold is cooled, opened and the formed article is removed from the mold.

The rotomolding cycle comprises three main steps, each of which has an impact on cycle time and the properties of the so-produced article. The three steps comprise:

-   -   sintering or coalescence,     -   densification or bubble removal, and     -   crystallization.

This is illustrated in FIG. 1 giving the air temperature in the mold, expressed in degrees centigrade, as a function of time, expressed in minutes, during an exemplary molding cycle. The first inflexion in the curve noted as point A marks the beginning of the sintering or coalescence of the polymer particles. Sintering in the present application represents the coalescence of the polymer particles. The next inflexion in the curve noted as point B marks the beginning of the densification process of the molten polymer. Densification in the present application means bubble removal. Throughout this application sintering and densification are seen as two distinct processes; they vary independently with the rotomolding parameters and with the resin properties.

Point C on the curve represents the Peak Internal Air Temperature (PIAT), followed by point D that marks the beginning of the crystallization process. Point E is associated with the time at which the rotomolded article is completely solidified and starts receding from the walls of the mold. Point F marks the opening of the mold, i.e. the end of the rotomolding cycle.

The present invention is mostly concerned with the modification of the polymer behavior in the sintering (coalescence) and densification (bubble removal) phases of the rotomolding cycle and slush molding cycle. Sintering is measured according to a method described for example by Bellehumeur et al. (C. T. Bellehumeur, M. K. Bisaria, J. Vlachopoulos, Polymer Engineering and Science, 36, 2198, 1996). Densification and bubble formation has been discussed by Kontopoulo et al. (M. Kontopoulo, E. Takacs, J. Vlachopoulos, Rotation, 28, January 2000). During melting air pockets or bubbles are trapped, thus delaying the formation of a homogeneous melt and also affecting the aesthetical and/or mechanical properties of the finished product.

For the present invention a charge-coupled device (CCD) camera was used to characterize the properties of polyolefin powders during a rotomolding cycle or during sintering and/or densification simulations.

EXAMPLES

Characterization of the processing behavior was analyzed using a megapixel progressive scan interline CCD with on-chip circuits commercially available from Kodak. It has the following characteristics:

-   -   architecture: interline CCD, progressive scan, non-interlaced     -   pixel count: 1000(H)×1000(V)     -   pixel size: 7.4 μm(H)×7.4 μm(V)     -   photosensitive area: 7.4 mm(H)×7.4 mm(V)     -   output sensitivity: 12 μV/electron     -   saturation signal: 40,000 electrons     -   dark noise: 40 electrons rms     -   dark current (typical): <0.5 nA/cm²     -   dynamic range: 60 dB     -   quantum efficiency at 500, 540, 600 nm: 36%, 33%, 26%     -   blooming suspension: 100×     -   image lag: <10 electrons     -   smear: <0.03%     -   maximum data rate: 40 MHz/channel (2 channels)     -   integrated vertical clock drivers     -   integrated correlated double sampling (CDS)     -   integrated electronic shutter driver

The high performance 15-bit (16 bits minus 1 bit for control) CCD sensor with transparent gate electrode provides 32,768 unsigned levels of gray, allows the acquisition of about 10,000 frames/s and covers a broad spectrum of from 400 to 1000 nm.

The camera set-up used to study sintering and densification behavior is illustrated in FIG. 2 with the CCD camera (1), the IR probe (2), the computer (3), the heating system (4) and the annular lighting system (5). A typical example for sintering is shown in FIG. 3 and a typical example for densification or bubble removal in FIG. 4.

The progressive disappearance of bubbles as a function of time and temperature is clearly and instantaneously followed. In addition to the visual aspect, the computer instantaneously produces a set of parameters resulting from picture analysis. These parameters are explained in Table I.

TABLE I Parameter Unit Description Ex — picture number t min time of picture T ° C. IR temperature of sample N — number of bubbles on the picture Na mm⁻² number of bubbles per mm² A μm² total area covered by bubbles Aa — percentage of total picture area covered by bubbles D_(av) μm average distance between 2 bubbles S μm² average area of one bubble Cr μm perimeter of one bubble based on Crofton's integral D_(eq) μm equivalent diameter of one bubble L μm largest side of one bubble W μm smallest side of one bubble LO degree orientation of the largest side WO degree orientation of the smallest side

The average distance between two bubbles D_(av) is defined as D _(av)=4(1−Aa)/Sv wherein Sv=4π(D_(eq)/2)²·Aa/((4π/3)(D_(eq)/2)³) wherein the equivalent bubble diameter D_(eq) is defined in terms of the average surface of one bubble S by the equation S=4π(D_(eq)/2)².

The base polyethylenes were supplied as pellets. The pellets were ground at 40 to 80° C. on commercial grinding equipment, e.g. a Wedco Series SE machine, to a powder with grain sizes from 100 μm to 800 μm. The processing aid or a blend of processing aids and a UV-stabilizer or a blend of UV-stabilizers were added to the powder in commercial mixing equipment.

Irganox® B 215 is a blend of Irgafos® 168 and Irganox® 1010 and is commercially available from Ciba Specialty Chemicals. Tinuvin® 783 is a UV-stabilizer commercially available from Ciba Specialty Chemicals. Cyasorb THT® 4611 and Cyasorb THT® 4802 are UV-stabilizers commercially available from Cytec Industries. Hytrel® 5556 can be obtained from Du Pont Company.

Examples 1 to 4 and Comparative Example 1

The polyethylene used for examples 1 to 4 and comparative example 1 was a monomodal polyethylene with a MI2 of 8.0 dg/min and a density of 0.934 g/ml; it was produced using a supported metallocene catalyst system. It is commercially available from Atofina under the name Finacene® M3582.

The processing aids, UV-stabilizers and other additives are given in Table II, together with their respective amounts.

The samples were evaluated on a 10 L canister prepared by rotomolding using a commercial rotomolding equipment. Peak Internal Air Temperature (PIAT) was 210° C. in all cases.

TABLE II Comp. Ex. 1 Ex. 1 Ex. 2 Ex. 3 Ex. 4 MI2 8.0 8.0 8.0 8.0 8.0 (dg/min) Density 0.934 0.934 0.934 0.934 0.934 (g/ml) Irganox ® 1500 1500 1500 1500 1500 B 215 (ppm) Zinc stearate 1500 (ppm) Hytrel ® 500 1000 500 500 5556 (ppm) Tinuvin ® 1500 783 (ppm) Cyasorb 1000 THT ® 4611 (ppm)

Using the polymer compositions of examples 1 to 4 rotomolded articles with a low number of bubbles could be obtained. 

The invention claimed is:
 1. A densification aid comprising: a polyetherester as a major component and a minor component selected from the group consisting of a fluoropolymer, a thermoplastic polyurethane, a polyether block copolyamide and polyethylene glycol; wherein the densification aid exhibits a capability of reducing bubble formation during rotomolding of particulate olefin polymer compositions.
 2. The densification aid of claim 1 wherein the polyetherester is a copolymer having polyester blocks and polyether blocks linked by ester linkages.
 3. The densification aid of claim 2 wherein the polyester blocks are condensation products of a diol selected from the group consisting of neopentyl glycol, cyclohexanedimethanol and an aliphatic glycol having the formula HO(CH₂)_(n)PH in which n is an integer within the range of 2-10, and an aromatic dicarboxylic acid having from 8-14 carbon atoms.
 4. The densification aid of claim 1, wherein the densification aid comprises at least some of the fluoropolymer in an amount less than the amount of said polyetherester.
 5. The densification aid of claim 4 wherein the fluoropolymer is a vinylidene fluoride homopolymer or copolymer.
 6. The densification aid of claim 1, wherein the densification aid comprises at least some of the thermoplastic polyurethane in an amount less that the amount of said polyetherester.
 7. An article comprising: a polyolefin composition comprising a densification aid, wherein the densification aid comprises a polyetherester as a major component and a minor component selected from the group consisting of a fluoropolymer, a thermoplastic polyurethane, a polyether block copolyamide and polyethylene glycol.
 8. The article of claim 7 wherein said polyetherester is a copolymer having polyester blocks and polyether blocks linked by ester linkages.
 9. The article of claim 8 wherein said polyester blocks are condensation products of a diol selected from the group consisting of neopentyl glycol, cyclohexanedimethanol and an aliphatic glycol having the formula HO(CH₂)_(n)OH in which n is an integer within the range of 2-10, and an aromatic dicarboxylic acid having from 8-14 carbon atoms.
 10. The article of claim 7 further comprising at least one UV stabilizer in an amount of no more than 0.5 weight percent based upon the amount of polyolefin composition.
 11. The article of claim 10, wherein the UV stabilizer is present in an amount within the range of 0.025-0.5 weight percent based upon the amount of said polyolefin composition.
 12. The article of claim 11 wherein said UV stabilizer is a hindered amine light stabilizer.
 13. The article of claim 7 wherein the polyolefin composition comprises an ethylene or propylene homopolymer or copolymer.
 14. The article of claim 13 wherein the polyolefin composition comprises an ethylene or propylene homopolymer or copolymer prepared by the polymerization of ethylene or propylene in the presence of a metallocene based polymerization system.
 15. The article of claim 7 wherein said densification aid comprises at least some of the fluoropolymer in an amount less than the amount of the polyetherester.
 16. The article of claim 15 wherein said fluoropolymer is vinylidene fluoride homopolymer or copolymer.
 17. The article of claim 7 wherein the densification aid comprises at least some of the thermoplastic polyurethane in an amount less that the amount of the polyetherester.
 18. The article of claim 7, wherein the densification aid exhibits a capability of reducing bubble formation during rotomolding of the article.
 19. The composition of claim 1, wherein the minor component comprises at least some of the polyether block copolyamide.
 20. The composition of claim 1, wherein the minor component comprises at least some of the polyethylene glycol. 